本系列产品以烧结镁砂或电熔镁砂、铬矿及其精矿、电熔镁铬砂等为主要原料，经高压成型、超高温烧结制备而成。镁铬砖可分为四类：普通硅酸盐结合镁铬砖、直接结合镁铬砖、半再结合镁铬砖、电熔再结合镁铬砖。
This series of products are mainly made of sinteredmagnesite or fused magnesite, chrome ore and itsconcentrate, fused magnesia-chrome sand. Magnesia-chrome brick canbe divided into four types: ordinary silicate-bondedmagnesia-chrome brick, direct-bonded magnesia-chrome brick,semi-bonded magnesia-chrome brick and fused re-bondedmagnesia-chrome brick.
普通镁铬砖是以MgO含量小于95的烧结镁砂和SiO2含量高的铬矿等为原料制备而成，其结合相为低熔相，常用于有色冶炼炉、玻璃窑、RH精炼炉等的衬。
Ordinary magnesia-chrome brick is made of sintered magnesia sandwith MgO content less than 95 and chromium ore with high SiO2content. Its binding phase is low-melting phase and it is oftenused in permanent lining of non-ferrous smelting furnaces, glasskilns and RH refining furnaces.
种类
Category
普通镁铬砖
Common Magnesia-Chrome Brick
CX-MGe
8A
CX-MGe
8B
12A
12B
CX-MGe
16A
16B
MgO % ≥
65
60
60
55
50
45
Cr2O3% ≥
8
8
12
16
16
显气孔率 Apparent Porosity % ≤
20
20
20
23
常温耐压强度
Cold Crushing Strength MPa ≥
35
30
30
35
荷重软化温度0.2Mpa R.U.L ℃ ≥
1620
1550
1580
1620
直接结合镁铬砖是以MgO含量大于95的优质烧结镁砂、SiO2含量较低的铬矿等为原料制备而成，其晶界液相少，以(Mg,Fe)(Fe,Al,Cr)2O4复合尖晶石为主，其直接结合程度高，具有强度高、抗热震稳定性好等优点，常用于RH精炼炉中上部槽工作衬、有色冶炼炉熔池、P-S铜转炉熔池、VOD炉熔池、玻璃窑及水泥回转窑烧成带等。
Direct-boned Magnesia-Chrome brick is made of high qualitysintered magnesia with the content of MgO more than 95 and chromeore with low content of SiO2 , with less liquid phase at grainboundary .It is mainly composed of (Mg,Fe)(Fe,Al,Cr)2O4 compositespinel, with a high degree of direct bonding, high strength andgood thermal shock stability. It is often used in the workinglining of middle groove and upper groove of RH refiningfurnace, melting pool of nonferrous smelting furnace, melting poolof P-S copper converter, melting pool of VOD furnace, firing zoneof glass kiln and cement rotary kiln.
种类
Category
直接结合镁铬砖
Direct-bonded Magnesia-Chrome Brick
CX-
ZMGe4
CX-
ZMGe6
CX-
ZMGe8A
CX-
ZMGe8B
CX-
ZMGe12A
CX-
ZMGe12B
ZMGe16A
ZMGe16B
ZMGe18A
ZMGe18B
MgO % ≥
80
75
74
74
66
66
60
58
58
Cr2O3% ≥
4
6
8
8
12
16
18
18
SiO2% ≤
2
2
1.5
2
1.5
2
显气孔率 % ≤
Apparent Porosity
18
18
18
18
常温耐压强度MPa ≥
Cold Crushing Strength
40
40
40
40
40
35
荷重软化温度℃ ≥
0.2Mpa R.U.L
1600
1600
1660
1600
1660
1600
电熔再结合镁铬砖是以电熔镁砂、电熔镁铬砂、铬精矿、铬绿等为原料制备而成，其结合相为高熔点(Mg,Fe)(Fe,Al,Cr)2O4复合尖晶石，其晶粒发育完善，具有高温强度高、抗冲刷性能及抗渣侵蚀性能好等优点，常用于RH精炼炉浸渍管及下部槽、有色冶炼炉、P-S铜转炉、闪速炉、VOD、精炼钢包等渣线区。
Fused reboned Magnesa-Chrome brick is made of fusedmagnesia, fused magnesia-chrome sand, chromium concentrate ,chromegreen sand and its combining phase is high melting point (Mg, Fe)(Fe, Al, Cr) 2 O4 compound spinel, its advantages are grainperfect development ,high temperature and high strength, erosionresistance and slag erosion resistance ,it is often used in dippipe and lower groove of the RH refining furnace, slagline area of non-ferrous smelting furnace, P - S copper converter,flash furnace, VOD, refining ladle .
种类
再结合镁铬砖
Rebonded Magnesia-Chrome Brick
CX-DMGe
20A
CX-DMGe
20B
24
26
MgO % ≥
65
60
60
52
50
Cr2O3% ≥
16
20
20
22
24
SiO2% ≤
1.2
1.6
1.2
显气孔率 % ≤
Apparent Porosity
16
常温耐压强度MPa ≥
Cold Crushing Strength
45
40
40
荷重软化温度℃ ≥
0.2Mpa R.U.L
1750
1700
1700
种类
Category
半再结合镁铬砖
Semi-rebonded Magnesia-Chrome Brick
CX-
BDMGe16A
BDMGe16B
CX-
BDMGe20A
CX-
BDMGe20B
MgO % ≥
60
55
55
Cr2O3% ≥
16
20
20
SiO2% ≤
1.5
2
1.5
2
显气孔率Apparent Porosity % ≤
17
17
17
常温耐压强度MPa ≥
Cold Crushing Strength
40
35
40
35
荷重软化温度0.2Mpa R.U.L℃ ≥
1750
1700
1750
1700
半再结合镁铬砖是以优质烧结镁砂、电熔镁砂、铬矿、电熔镁砂为原料制备而成，其性能介于直接结合镁铬砖与电熔再结合镁铬砖之间，具备强度高、抗渣性能及抗热震稳定性好等优点，常用于各种高温冶炼炉的风眼区，如P-S铜转炉、炼铜阳极炉等。
Semi-reboned Magnesite-Chrome brick is made of the highquality sintered magnesia, fused magnesia, chrome ore , and itsperformance between direct-boned Magnesia-Chrome bricks and fusedreboned Magnesia-Chrome brick, with advantages of high strength,good slag resistance and thermal shock stability, etc, they areoften used in f eye area of all kinds of high temperature furnaces, such as P -s copper converter, refined copper anode furnace,etc.